GOST 9466, GOST 9467 Е41 2(4) – B20 SFA/AWS E6015 EN E 35 3 В 22 For manual arc welding of heavy duty constructions from carbon and low-alloyed steel grades, when weld metal is required to possess very good plasticity and impact toughness.
|
GOST 9466, GOST 9467 Е43 3 B20 SFA/AWS E6015 EN E 35 3 В 2 2 For welding of heavy duty constructions from carbon and low-alloyed steel grades with the tensile strength of up to 590 MPa (60 kgf/mm2) in all positions, except vertical down.
|
|
|
GOST 9466, GOST 9467 Е51 4 B20 SFA/AWS E7015 EN E 38 3 B 2 2 For welding of heavy duty constructions from carbon and low-alloyed steel grades, when weld metal is required to possess very good plasticity and impact toughness.
|
GOST 9466, GOST 9467 E 51 5 B26 SFA/AWS E7016 EN: E 42 4 1Ni B12 For welding the joints of oil and gas pipelines of carbon and low-alloyed steel, constructions of sea stationary platforms under temperature not low than -40ºC
May be used in the sea ships constructions.
|
|
|
E 43 2(3) RC13 SFA/AWS E6013 EN: E 35 2 RС 1 1 For welding the joints of oil and gas pipelines of carbon and low-alloyed steel diameter from 59 up to 142 mm when underground workings.
|
GOST 9466, GOST 9467 E 43 0(3) R26 SFA/AWS E 6013 EN: E 35 2 R 1 2 For welding of heavy duty constructions from carbon steel grades with the carbon content of up to 0,25% in all positions, except vertical down.
|
|
|
GOST 9466, GOST 9467 E 43 0(3) R21 SFA/AWS E6013 EN: E 35 2 R 1 2 For welding of constructions from carbon steel grades with the content of carbon of up to 0,25%
|
GOST 9466, GOST 9467 E 43 2(3) R12 SFA/AWS E6013 EN: E 35 2 R 1 1 For welding of carbon and low-alloyed structural steel grades with the carbon content of up to 0,25%
|
|
|
GOST 9466, GOST 9467 E 43 0(3) RA24 SFA/AWS E6013 EN: E 35 2 RА 1 2 For welding of constructions from low-carbon steel grades with the carbon content of up to 0,22% in all positions, except vertical down.
|
GOST 9466, GOST 9467 E 43 0(3) RA26 SFA/AWS E 6013 EN: E 35 2 RA 1 2 For welding of constructions from low-carbon steel grades in all positions, except vertical down.
|
|
|
New
GOST 9466, GOST 9467 E 43 2(3) R11 SFA/AWS E 6013 EN: E 35 2 R 1 1 For welding of constructions from carbon steel grades in all welding positions.
|
GOST 9466, GOST 9467 E 43 2(3) RC13 SFA/AWS E6013 EN: E 35 2 RС 1 1 For welding in all positions of ordinary and heavy duty constructions from low-carbon steel grades.
|
|
|
New
GOST 9466, GOST 9467 Е51 4 – B20 SFA/AWS A5.1:E7015 EN: E 38 0 В 2 2 H 1 0 For welding of heavy duty constructions from carbon and low-alloyed steel grades, when weld metal is required to possess very good plasticity and impact toughness, especially at low temperatures.
|
GOST 9466, GOST 10052 E 2005 B20 SFA/AWS E 25 12 B20 EN E 308 15 For welding cast and rolled metal made of highly heat resisting steels of grade 20Х23N13, 20Х23N18 and similar, working in oxidizing medium for temperatures 1000ºC with high demands to resistance to intercrystalline corrosion.
|
|
|
GOST 9466, GOST 10052 Е2004 B20 SFA/AWS E 19 9 B20 EN E 309 15 For welding of corrosion resistant stainless steel equipment of grade 08Х18N10, 12Х18N9, 08Х18N10Т and similar, when there is no high demands to resistance to intercrystalline corrosion.
|
GOST 9466-75 Е23 12 B20 SFA/AWS E309-15 EN E 38 0 В 2 2 H 1 0 For cold welding of structures of high strength cast iron with a spheroid graphite and of grey cast iron with lamellar graphite and their combinations with steel, for repairing of defects in castings and for preliminary depositing of the first 1-2 layers upon worn out cast iron parts as preparation for subsequent depositing with special types of electrodes.
|
|
|
GOST 9466-75 10051-75 Е23.12 B20 SFA/AWS E309-15 EN: E 38 0 В 2 2 H 1 0 For hardfacing on materials with very high strength and ductility
|
GOST 9466-75 10051-75 Е23.12 B20 SFA/AWS E309-15 EN: E 38 0 В 2 2 H 1 0 For hardfacing on materials with moderate strength and ductility
|
|